The precise controllability of the Fermi level is a critical aspect of quantum materials. For topological Weyl semimetals, there is a pressing need to fine-tune the Fermi level to the Weyl nodes and unlock exotic electronic and optoelectronic effects associated with the divergent Berry curvature. However, in contrast to two-dimensional materials, where the Fermi level can be controlled through various techniques, the situation for bulk crystals beyond laborious chemical doping poses significant challenges. Here, we report the milli-electron-volt (meV) level ultra-fine-tuning of the Fermi level of bulk topological Weyl semimetal tantalum phosphide using accelerator-based high-energy hydrogen implantation and theory-driven planning. By calculating the desired carrier density and controlling the accelerator profiles, the Fermi level can be experimentally fine-tuned from 5 meV below, to 3.8 meV below, to 3.2 meV above the Weyl nodes. High-resolution transmission electron microscopy reveals the crystalline structure is largely maintained under irradiation, while electrical transport indicates that Weyl nodes are preserved and carrier mobility is also largely retained. Our work demonstrates the viability of this generic approach to tune the Fermi level in semimetal systems and could serve to achieve property fine-tuning for other bulk quantum materials with ultrahigh precision. 

Abstract Performance of the group IV monochalcogenide GeSe in solar cells, electronic, and optoelectronic devices is expected to improve when high‐quality single crystalline material is used rather than polycrystalline films. Crystalline flakes represent an attractive alternative to bulk single crystals as their synthesis may be developed to be scalable, faster, and with higher overall yield. However, large – and especially large and thin – single crystal flakes are notoriously hard to synthesize. Here it is demonstrated that vapor‐liquid‐solid growth combined with direct lateral vapor‐solid incorporation produces high‐quality single crystalline GeSe ribbons with tens of micrometers size and controllable thickness. Electron microscopy shows that the ribbons exhibit perfect equilibrium (AB) van der Waals stacking order without extended defects across the entire thickness, in contrast to the conventional case of substrate‐supported flakes where material is added via layer‐by‐layer nucleation and growth on the basal plane. Electrical measurements show anisotropic transport and a high Hall mobility of 85 cm² V⁻¹ s⁻¹, on par with the best single crystals to date. Growth from mixed GeSe and SnSe vapors, finally, yields ribbons with unchanged structure and composition but with jagged edges, promising for applications that rely on ample chemically active edge sites, such as catalysis or photocatalysis.